dc.identifier.citation | SANTOS, Ricardo Baeta. Utilização de resíduos ricos em óxidos de ferro e cromo para redução de silício em aços inoxidáveis recicláveis. 2013. 104 f. Dissertação (Mestrado em Engenharia Metalúrgica e de Materiais) - Instituto Ferderal do Espírito Santo, Vitória, 2013 | pt_BR |
dc.identifier.uri | https://repositorio.ifes.edu.br/xmlui/handle/123456789/308 | |
dc.description.abstract | RESUMO: Nos processos metalúrgicos, atualmente, a reciclagem de metais e ligas é uma pratica comum e geralmente existe a necessidade de se eliminar algumas impurezas. O aproveitamento de sucatas é uma alternativa que melhora a cadeia produtiva. Este contexto justifica o desenvolvimento de técnicas que objetivam remover impurezas dos metais fundidos e ligas. Os aços inoxidáveis são de elevado custo de produção devido a presença de elementos nobres tais como cromo, níquel, manganês entre outros. O objetivo deste trabalho foi viabilizar o aproveitamento de sucatas de aço inoxidável com concentrações de Si superior a 1% em peso. As indústrias metalúrgicas, em especial fundições que usam sucatas fundidas em fornos elétricos a arco ou de indução podem remover o silício em excesso através da adição de resíduos ricos em oxigênio no processo. Os resíduos podem ser, por exemplo, a carepa de lingotamento contínuo e/ou pós gerados no sistema de tratamento e limpeza de gases de aciaria, ambos ricos em FeO. Quando estes materiais são adicionados na superfície do banho metálico promovem a oxidação do silício além de outros elementos e proporcionam sua conseqüente redução percentual. A remoção do silício além de viabilizar o uso de maior quantidade de sucata, favorece também o ajuste de composição química de outros elementos tais como o cromo e o manganês, através do uso de ferros-liga com menor nível de pureza logo, menor custo. Como exemplo específico, o processo viabiliza o uso de FeMn75 com Si ao invés de Mn eletrolítico. Sucatas de aços inoxidáveis para fundição do tipo A297HH foram fundidas e adicionou-se resíduos ricos em FeO sob temperatura constante. Mediu-se então a composição química do aço em função do tempo. As temperaturas estudadas nos experimentos realizados variaram de 1450°C até 1525C°. Os resultados mostram que o processo é sensível a temperatura e mais rápido quando esta é mais elevada. Verificou-se também, que sob temperaturas mais baixas consegue-se remover o silício com menores perdas de cromo. | pt_BR |
dc.description.abstract | ABSTRACT: In metallurgical processes currently the recycling of metals and alloys is a common
practice and generally there is a need to remove some impurities. Depending on the
value of the product may be viable or not to remove them. The use of scrap is an
alternative that improves supply chain. This context justifies the development of
techniques that aim to remove impurities from molten metals and alloys. Stainless
steels are steels that are resistant to corrosion when exposed to aggressive agents.
The chemical composition of these alloys ensures this property, but is costly because
of the presence of noble elements such as chrome, nickel, manganese, among
others. This work was possible the utilization of scrap stainless steel with Si
concentrations greater than 1% by weight. The metallurgical industries, especially
foundries that use scrap melted in electric arc furnaces or induction may remove the
excess silicon by adding industrial waste rich in iron oxide. The materials may be, for
example, mill scale continuous casting and / or powders generated in the treatment
system and cleaning of flue gases, both high in FeO. When these materials are
added to the surface of the metal bath promotes the oxidation of silicon and other
elements and provide a consequent reduction percentage. The removal of silicon in
addition to allowing the use of larger amount of scrap also favor the chemical
composition adjustment of other elements such as chrome and manganese, by using
iron-alloy with lower purity hence lower cost. In this work merged stainless steel
scrap to melt, more particularly the types HH and was added industrial waste with
iron oxide and chrome at constant temperature. Was then measured the chemical
composition of the steel as a function of time. Temperatures studied in experiments
ranged from 1450°C to 1525°C. The results show that the process is sensitive to
temperature and faster when it is higher. The removing of silicon with reduced loss of
chrome is achieved in lower temperatures. | |
dc.language.iso | por | pt_BR |
dc.rights | Acesso Aberto | |
dc.subject | Produção | pt_BR |
dc.subject | Reaproveitamento | pt_BR |
dc.subject | Aço inoxidável | pt_BR |
dc.subject | Metais | |
dc.subject | Aço | |
dc.title | Utilização de resíduos ricos em óxidos de ferro e cromo para redução de silício em aços inoxidáveis recicláveis | pt_BR |
dc.type | Dissertação de mestrado | pt_BR |
dc.contributor.advisor-co | Oliveira, José Roberto de | |
ifes.campus | Campus Vitória | |
ifes.underposgraduate | Programa de Pós-graduação em Engenharia Metalúrgica e de Materiais | |
dc.identifier.capes | 30004012001P0 | |
Redes Sociais